influence of modulated structure on magnetic properties of NdFeB/Co multilayer thin films
Fu Yu-dong(傅宇东), Wang Shi-yang(王诗阳), Zhu Xiao-shuo(朱小硕), Fang Bo(方博), Yan Feng(闫峰)

College of Materials Science and Chemical Engineering, Harbin Engineering University, Harbin 150001, China

Abstract:The NdFeB/Co multilayer films were prepared by magnetron sputtering. After that, the samples were annealed at 600 °C for 20 min. The surface morphology, phase structures and magnetic properties of Mo (50 nm)/[NdFeB (100 nm)/Co(y)]×10/Mo (50 nm) thin films were researched by AFM, XRD and VSM, respectively. The results show that the films show stronger perpendicular magnetic anisotropy. When the thickness of Co layers is 10 nm, the coercivity Hc is the maximum, 295 kA/m. However, for y=10-20, the reduced remanence M/Ms of films has increased. When the thickness of Co layers is 20-30 nm, the NdFeB/Co multilayer films obtained more superior magnetic properties with M/Ms =0.95.

 

Key words: NdFeB/Co film; modulated structure; perpendicular magnetic anisotropy; coercivity; reduced remanence

中南大学学报(自然科学版)
  ISSN 1672-7207
CN 43-1426/N
ZDXZAC
中南大学学报(英文版)
  ISSN 2095-2899
CN 43-1516/TB
JCSTFT
版权所有:《中南大学学报(自然科学版、英文版)》编辑部
地 址:湖南省长沙市中南大学 邮编: 410083
电 话: 0731-88879765(中) 88836963(英) 传真: 0731-88877727
电子邮箱:zngdxb@csu.edu.cn 湘ICP备09001153号