Laboratory investigation on effects of organic montmorillonite on performance of crumb rubber modified asphalt
TAN Zhi-hua(谭志华)1, WANG Ji-jing(王觊婧)2, SHI Zhen-ning(史振宁)2

1. School of Physical Education, Changsha University of Science & Technology, Changsha 410004, China;
2. School of Traffic & Transportation Engineering, Changsha University of Science & Technology,
Changsha 410004, China

Abstract:In this paper, organic montmorillonite (OMMT) was added into crumb rubber modified asphalt(CRMA) to improve its high temperature performance, anti-aging performance and storage stability. The effects of different OMMT content on properties of CRMA were studied. The rutting factor obtained by dynamic shear rheological (DSR) test was adopted to evaluate the high-temperature performance. The creep stiffness and m value determined by the bending beam rheometer (BBR) test were employed to evaluate the low-temperature performance. The softening point, ductility, rutting factor before and after rolling thin film ovens test (RTFOT) and pressure aging vessel test (PAV) were compared to characterize the aging properties. Moreover, the segregation test after being reserved for 48 h and 7 d was conducted, and the softening point and rutting factor of upper and lower layers of segregation pipe were adopted to evaluate the storage stability. The results indicated that the high-temperature performance and anti-aging performance were developed with the increasing content of OMMT, while the low-temperature performance deteriorated. The storage stability was improved with the increasing content of OMMT before the content exceeded 4%, after which the storage stability declined. Taking account of all factors, it is suggested that the optimum content of OMMT is 3%-4%.

 

Key words: crumb rubber modified asphalt; organic montmorillonite; high-temperature performance; low-temperature performance; storage stability.

中南大学学报(自然科学版)
  ISSN 1672-7207
CN 43-1426/N
ZDXZAC
中南大学学报(英文版)
  ISSN 2095-2899
CN 43-1516/TB
JCSTFT
版权所有:《中南大学学报(自然科学版、英文版)》编辑部
地 址:湖南省长沙市中南大学 邮编: 410083
电 话: 0731-88879765(中) 88836963(英) 传真: 0731-88877727
电子邮箱:zngdxb@csu.edu.cn 湘ICP备09001153号